Isifinyezo
I-OBC-35S iyisengezo sokulahlekelwa uketshezi lwe-polymer kasimende osetshenziswa kumthombo kawoyela futhi yakhiwe nge-copolymerization ene-AMPS njenge-monomer eyinhloko enezinga lokushisa elihle nokumelana nosawoti futhi ihlanganiswe namanye ama-monomers aphikisana nosawoti.Ama-molecule aqukethe inani elikhulu lamaqembu akhangayo kakhulu njenge-CONH2, - SO3H, - COOH, edlala indima ebalulekile ekuphikiseni usawoti, ukumelana nezinga lokushisa, ukumuncwa kwamanzi amahhala, ukunciphisa ukulahlekelwa kwamanzi, njll.
I-OBC-35S inokuguquguquka okuhle futhi ingasetshenziswa ezinhlelweni ezihlukene zodaka lukasimende.Inokuhambisana okuhle nezinye izithasiselo futhi ibamba iqhaza ekukhuthazeni i-viscosity nokumiswa ngenxa yesisindo esikhulu samangqamuzana.
I-OBC-35S ifanele izinga lokushisa elibanzi elinokumelana nezinga lokushisa elifinyelela ku-180℃.Ngemuva kokusetshenziswa, i-fluidity yesistimu ye-slurry kasimende yinhle, izinzile ngoketshezi oluncane lwamahhala futhi ngaphandle kwesethi yokuhlehlisa namandla akhula ngokushesha.
I-OBC-35S ilungele ukuxutshwa kodaka lwamanzi/amanzi anosawoti.
Idatha yobuchwepheshe
| Into | Index |
| Ukubukeka | Impushana emhlophe |
Ukusebenza kodaka lukasimende
| Into | Tinkomba yezobuchwepheshe | Isimo sokuhlola |
| Ukulahlekelwa kwamanzi, ml | ≤100 | 80℃,6.9MPa |
| Isikhathi sokuqina, imiz | ≥60 | 80℃,45MPa/45min |
| Ukungaguquguquki kokuqala, Bc | ≤30 | |
| Amandla acindezelayo, i-MPa | ≥14 | 80 ℃, ingcindezi evamile, 24h |
| Amanzi amahhala, ml | ≤1.0 | 80 ℃, ingcindezi evamile |
| Ukwakhiwa kwe-Cement slurry: 100% we-G grade usimende (ukumelana nesulfure ephezulu) + 44.0% amanzi ahlanzekile + 0.7% OBC-35S + 0.5% defoamer. | ||
Ibanga lokusetshenziswa
Izinga lokushisa: ≤180°C (BHCT).
Umthamo ophakanyisiwe: 0.6% -3.0% (BWOC).
Iphakheji
I-OBC-35S ipakishwe esikhwameni esingu-25kg esiyinhlanganisela yezinto ezintathu-in-one, noma ipakishwe ngokwezidingo zekhasimende.
Phawula
I-OBC-35S ingahlinzeka ngemikhiqizo ewuketshezi i-OBC-35L.