Summary
OBC-41S is a polymer oil well cement fluid loss additive. It is copolymerized with AMPS/NN, which has good resistance to temperature and salt, as the main monomer, combined with other salt-tolerant monomers. The product introduces groups that are not easily hydrolyzed, the high temperature resistance is obviously enhanced, and the molecule contains a large number of strong adsorption groups such as -CONH2, -SO3H, -COOH, which play an important role in temperature resistance, adsorption of free water, and loss of water.
OBC-41S has good versatility, can be used in a variety of cement slurry systems, and has good compatibility with other additives.
OBC-41S has a high low shear rate viscosity, which can effectively enhance the suspension stability of the cement slurry system, while maintaining the fluidity of the slurry, preventing sedimentation, and having good gas channeling resistance.
OBC-41S has a wide application temperature, high temperature resistance up to 230℃, good fluidity and stability of the cement slurry system, less free liquid, no retardation, and rapid development of early strength at low temperature.
OBC-41S is suitable for fresh water slurry preparation.
Technical data
|
Item |
index |
|
Appearance |
White powder |
Cement slurry performance
|
Item |
Technical index |
Test condition |
|
Water loss，mL |
≤100 |
80℃,6.9MPa |
|
Thickening time, min |
≥60 |
80℃,45MPa/45min |
|
Initial consistency,Bc |
≤30 |
|
|
Compressive strength, MPa |
≥14 |
80℃,normal pressure,24h |
|
Free water, mL |
≤1.0 |
80℃,normal pressure |
| Cement slurry composition: 100% G grade cement (high sulfur resistance) + 44.0% fresh water + 0.6% OBC-41S + 0.5% defoamer. | ||
Usage range
Temperature: ≤230°C (BHCT).
Suggestion dosage: 0.6%-3.0% (BWOC).
Package
OBC-41S is packed in a 20kg three-in-one compound bag, or packed according to customer requirements.
Remark
OBC-41S can provide liquid products OBC-41L.